Such thing as over-fluxing?

When I melt down old plumbing pipe, etc., I flux a couple times to remove a lot of gunk and pour into ingots.
Then at a later date I melt it down again with tin and an antimony alloy to make my final casting alloy ingots (usually 92/4/4), I flux it a couple times and pour into finished ingots.
THEN in the future I melt it down and flux at least once again before I start casting bullets.
Am I normal? Or is this overkill? Is there any dis-advantage to over-fluxing?
Thanks, Steve W.
Circa 1964: Rocky to Bullwinkle:
"But that trick never works!"
But Bullwinkle tries it anyway...again and again
steve1147 is offline  
Old March 24, 2011, 07:08 PM   #2
Senior Member
Join Date: August 1, 2007
Location: Tabor City , NC.
Posts: 1,970
I flux till stuff quits coming to the top , & while it`s in the smelting pot I like to flux it HOT !!!

I`ll average 8-14 times !!!
GP100man is offline  

Thread Tools Search this Thread
Search this Thread:

Advanced Search

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump

All times are GMT -5. The time now is 07:19 PM.

Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2017, vBulletin Solutions, Inc.
This site and contents, including all posts, Copyright © 1998-2017 S.W.A.T. Magazine
Copyright Complaints: Please direct DMCA Takedown Notices to the registered agent:
Contact Us
Page generated in 0.04048 seconds with 7 queries