How to soften linotype lead
I need to soften my linotype lead to a more desirable hardness level similar to WW lead. I would appreciate any suggestions on how to do this?
|
September 9, 2010, 04:24 AM | #2 |
Senior Member
Join Date: October 28, 2006
Location: South Central Michigan...near
Posts: 6,501
|
Your post begs the question: Why? Linotype is sought after by bullet casters. Many would be happy to trade wheel weights or plumbers lead for your Linotype. Nevertheless, if you add enough "plumbers lead" to your Linotype, it will result in a softer alloy...that is the only way to soften it.
|
September 9, 2010, 08:07 AM | #3 |
Staff
Join Date: April 13, 2000
Location: Northern Virginia
Posts: 41,388
|
I thought wheel weights were generally a little harder than lino?
__________________
"The gift which I am sending you is called a dog, and is in fact the most precious and valuable possession of mankind" -Theodorus Gaza Baby Jesus cries when the fat redneck doesn't have military-grade firepower. |
September 9, 2010, 08:22 AM | #4 |
Senior Member
Join Date: April 25, 2010
Location: Arkansas
Posts: 3,309
|
Old wheel weights were fairly hard, not much different than linotype.
But, I would shy away from wheel weights these days as new ones are no longer lead. You could get inconsistent, and dissapointing results with new wheel weights. For pistol, the linotype, as is, should be pretty good. It softens when it is melted. |
September 9, 2010, 09:27 AM | #5 | |
Senior Member
Join Date: October 28, 2006
Location: South Central Michigan...near
Posts: 6,501
|
Quote:
Wheel Weights are still the most available source of lead in most of the country inasmuch as salvage yards still have (and will have as long as old cars have them on their wheels), lead wheel weights despite the movement to non-lead (steel, zinc). Many areas have little-no source for Linotype and rely on Wheel Weights plus a little tin for all our bullet casting. When Linotype is found, it is pounced upon by casters like a duck on a June bug. http://home.earthlink.net/~potomac008/Lead%20Alloys.htm (bullet alloy composition: Copyright 2001 2009- 13th Confederate Infantry) http://castboolits.gunloads.com/showthread.php?t=42016 (Bullet alloys: castboolit.gunloads.com forum) Last edited by dahermit; September 9, 2010 at 06:49 PM. |
|
September 9, 2010, 09:59 AM | #6 |
Senior Member
Join Date: November 22, 2006
Posts: 3,077
|
I have quite a bit of Linotype that a printer friend gave me and it is harder than the WW lead that I have. As said above I just cut in pure lead until bullets drop out of the mold at the advertised weight (a pure Linotype bullet is light).
|
September 9, 2010, 03:29 PM | #7 |
Staff
Join Date: March 4, 2005
Location: Ohio
Posts: 21,061
|
Lyman lists linotype as having a BHN of 22, and wheel weights (not hardened) as having a BHN of 9. And that's for good wheel weights. I have run into softer ones.
Lyman #2 is listed with a BHN of 15. That is the exact same BHN they give for 50:50 linotype with pure lead. So, mix in an equal weight of pure lead with your linotype to arrive at the same hardness as #2 alloy. What you will end up with is about 2% tin and 6% antimony. This mix is also known as Teracorp magnum bullet alloy. It is not as pretty looking as #2 because it has less tin in it, but works pretty well. Another approach would be to put 6½ pounds of linotype, 8 pounds of lead, and 8 ounces of lead-free plumbing solder (which is mostly tin) together. That will be very close to actual Lyman #2 alloy. Do be careful to double-check the MSDS of the lead-free plumbing solder online to make sure the brand you buy includes no zinc, but I don't believe much of it does. Zinc spoils mold fillout. Might want to ask a moderator to move this thread to the cast bullet forum? You'll maybe get still more answers there?
__________________
Gunsite Orange Hat Family Member CMP Certified GSM Master Instructor NRA Certified Rifle Instructor NRA Benefactor Member and Golden Eagle |
September 9, 2010, 10:00 PM | #8 |
Senior Member
Join Date: September 8, 2010
Location: New Mexico
Posts: 688
|
So is plumber's lead considered pure lead? I have linotype and plumbers lead laying around for a rainy day.
|
September 10, 2010, 01:10 PM | #9 | |
Senior Member
Join Date: October 28, 2006
Location: South Central Michigan...near
Posts: 6,501
|
Quote:
|
|
September 12, 2010, 04:06 PM | #10 |
Member
Join Date: October 27, 2009
Posts: 22
|
5 parts PB to 1 part Lino (12% Sb) boolit's water dropped will give you about 12 Bhn, same as air cooler WW's. Check here for other mixes. http://www.lasc.us/CastBulletNotes.htm
I'm currently using Case Monotype (24% Sb) at 9:1 for around 15 Bhn after dropped in water for 18hrs. or so. |
September 25, 2010, 10:54 PM | #11 |
Senior Member
Join Date: May 29, 2008
Location: now living in alabama
Posts: 2,433
|
I found that straight linotype would splatter on a metal target using my rcbs kieth 250gr GC. Straight WW seemed to lead a bit. I found that if I use 4 parts WW to 1 part linotype, the leading is down to a minimum, they drive a bit deeper into the target, and they dont splatter. They also form sharper edges from the mold.
__________________
No such thing as a stupid question. What is stupid is not asking it. |
September 26, 2010, 02:43 PM | #12 |
Member
Join Date: September 5, 2010
Posts: 65
|
The " stick on, double sided tape on" wheel weights are darn near pure lead, adding some of them to the batch should soften your harder alloy.
|
October 10, 2010, 03:04 AM | #13 |
Member
Join Date: August 16, 2010
Location: North Central Texas
Posts: 31
|
Linotype is 4-12-84 Tin/Antomony/Lead
If you want the standard commercial cast bullet alloy mix it 50/50 with lead to get 2-6-92 with a bnh of about 15 a couple weeks after casting. Even air cooled alloy hardend with age but , not nearly as much as water dropped. Mix 3 leads with 1 lino to get typical WW equivelant alloy. And since so many casters mix their clip-on WWs 50/50 with lead , you could even 5 parts lead and do just fine for most handguns.
__________________
Leslie |
November 10, 2010, 08:53 PM | #14 |
Senior Member
Join Date: June 4, 2007
Location: Upstate SC
Posts: 1,943
|
I use 50/50 lino and pure to get 7.5% antimony shot. Works fine for magnum bullets and slower rifle calibers like 30-30, 30-40, 35, and 32 Spl.