Casting 58 cal minie balls with 20-1 alloy.
I just purchased a reproduction 1853 enfield. I have about 30 lbs of 20 parts lead to 1 part tin alloy which I use to make bullets for black powder cartridges. I know that pure lead is generally recommended for making minies, but can I get away with using the 20-1 alloy I already have? It would be nice if in the future I could use the same lead for cartridges and minie balls. Would it make sense to change to a 30-1 or 40-1 alloy next time I order a bunch of lead?
|
August 21, 2017, 07:04 AM | #2 |
Senior Member
Join Date: July 26, 2011
Location: USA
Posts: 1,730
|
20/1 is 10 BHN. Pure is 5 from Lyman chart. The hollow base needs to expand on firing.
I would guess it depends on how much powder is used and the amount of pressure needed to expand the base. Looks like some testing is in order. |
August 21, 2017, 07:40 AM | #3 |
Senior Member
Join Date: June 17, 2010
Location: Virginia
Posts: 6,869
|
If it works (I've already used pure lead), it works.
Try it. But I'd sure use the thin skirt Lyman Minnie ball |
August 21, 2017, 07:46 AM | #4 | |
Senior Member
Join Date: May 27, 2007
Posts: 5,261
|
Quote:
__________________
If I'm not shooting, I'm reloading. |
|
August 21, 2017, 10:11 AM | #5 |
Staff
Join Date: March 4, 2005
Location: Ohio
Posts: 21,022
|
That's one potential problem. The harder alloy is also more brittle. The skirts may lose portions at exit from muzzle blast. I suppose you could always drill muzzle brake holes into the barrel near the muzzle to drop the pressure more, but that kind of messes with the authenticity of the reproduction, not to mention creating a potential cleaning nightmare. However, if the barrel is long enough, you may be OK.
Another potential problem is the harder material failing to be impressed into the rifling hard enough at the inside corners make a complete enough seal. In that event you'll get bad leading as well as poor accuracy.
__________________
Gunsite Orange Hat Family Member CMP Certified GSM Master Instructor NRA Certified Rifle Instructor NRA Benefactor Member and Golden Eagle |
Tags |
black powder , casting , lead , minie |