Nothing wrong with your rifle. It's the ammo.

Those commies were cheap bastards. They cut corners to extremes on production. The steel in those cases was extruded too far without being annealed, and it developed longitudinal weaknesses. If you closely examine a few dozen unfired rounds out of that spam can, you'll probably find several other rounds with the beginnings of cracks showing. If you closely examine all your fired rounds, you'll probably find several others that have cracked. That is very common. It happens to me all the time. The only noticeable problem from it is that the bolt can be a little sticky on the cracked cases. If it scares you, don't shoot any more steel cased commie surplus ammo.
leadchucker is offline  
Old March 25, 2012, 08:23 PM   #27
Senior Member
Join Date: January 11, 2011
Posts: 374
yup prob the'll notice this with 70 year old turk 8mm mauser ammo too! heck sometimes the case will already be split before you shoot it lol
triumph666 is offline  

7.62x54r , ammo , headspace

Thread Tools Search this Thread
Search this Thread:

Advanced Search

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump

All times are GMT -5. The time now is 05:16 PM.

Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2017, vBulletin Solutions, Inc.
This site and contents, including all posts, Copyright © 1998-2017 S.W.A.T. Magazine
Copyright Complaints: Please direct DMCA Takedown Notices to the registered agent:
Contact Us
Page generated in 0.04680 seconds with 10 queries