Quote:
Originally Posted by johnwilliamson062
What makes you think it holds up on interiors of barrels or on slides? I would love to see a gun with 70K rounds through it that has any cerakote left on any wear surfaces.
Actually, 10K would surprise me.
I would be surprised if there were no spots where it wore through after 5k.
I will clarify that Nitriding does not technically qualify as a coating as it is a material treatment. Nothing is added, rather the metal is changed.
|
Who said anything about the "interior" of barrels? Your one of those guys that don't even read the threads and just ramble aren't you?