Is my caspian slide stainless steel?

Attached pic is the underside showing the batch number I think, there is no S mark for stainless, but the seller said it is stainless.



Anyways for me to know if it is stainless?
glenjoy is offline  
Old November 22, 2008, 09:29 PM   #2
Unclenick
Staff
 
Join Date: March 4, 2005
Location: Ohio
Posts: 9,997
Austenitic stainless steels don't attract a magnet. Other grades have enough chrome an nickel that they don't attract a magnet as well as carbon steel, so you can use a magnet to compare the two. Otherwise, if it has no finish, you will find acid acts a good deal more slowly on stainless than on regular carbon steel. It shouldn't have any rusty fingerprints on it, either. A good test liquid would be a rust bluing solution. It will raise fine rust over a day on conventional carbon steels, but not on stainless in any significant degree.
__________________
Gunsite Orange Hat Family Member
CMP Certified GSM Master Instructor
NRA Certified Rifle Instructor
NRA Patron Member
Unclenick is offline  
Old November 23, 2008, 12:34 PM   #3
Michaelm45
Senior Member
 
Join Date: October 28, 2004
Location: NV
Posts: 215
Why not call and ask?
Michaelm45 is offline  
Old November 23, 2008, 06:49 PM   #4
Scorch
Senior Member
 
Join Date: February 13, 2006
Location: Washington state
Posts: 11,342
I test supposedly stainless steel parts with cold blue. It won't darken stainless steel.

Quote:
Why not call and ask?
Good idea. Call Caspian.
__________________
Never try to educate someone who resists knowledge at all costs.
But what do I know?
Summit Arms Services
Taylor Machine
Scorch is offline  
Old November 23, 2008, 08:02 PM   #5
oldcspsarge
Senior Member
 
Join Date: January 11, 2008
Location: Rocky Mountains
Posts: 436
Original S&W stailness steel revolvers wouls not attract a magnet....
but those days are gone. All of todays stainless will attract a magnet
AND will rust !

There is absolutely no reason to buy stainless today unless you like the look !
oldcspsarge is offline  
Old November 23, 2008, 08:07 PM   #6
Bill DeShivs
Senior Member
 
Join Date: April 7, 2006
Posts: 6,889
Original S&W guns would rust, too.
Stainless is not rust proof, but it resists rust much better than carbon steel. Even if it does rust, it is not usually bad enough to hurt function.
Stainless requires minimal surface care.
__________________
Bill DeShivs
www.billdeshivs.com
Bill DeShivs is online now  
Old November 24, 2008, 02:00 AM   #7
Unclenick
Staff
 
Join Date: March 4, 2005
Location: Ohio
Posts: 9,997
The tool maker where I worked in the 70's used to distinguish what he called "true" stainless from the other alloys. He said true stainless was one particular alloy, used mainly in surgical instruments and implants, but which was not tough enough for many applications, guns and hunting knives, included. It was an austenitic stainless in the 300 series, IIRC. Today there are both austenitic and martensitic stainless alloys for medical applications. I guarantee they don't want someone with a knee replacement either rusting out or attracting the magnet in the MRI machine.

The stainless Buck hunting knife sitting on my workshop table attracts a magnet and will rust a little, but it does neither as well as conventional carbon steel. It's the comparison you want to look for. The cold blue test is a good one. They do make cold blue for stainless, but it really doesn't work as fast as cold blues for regular steel, nor is the result as dark, being more like a charcoal gray.
__________________
Gunsite Orange Hat Family Member
CMP Certified GSM Master Instructor
NRA Certified Rifle Instructor
NRA Patron Member
Unclenick is offline  
Old November 26, 2008, 12:11 PM   #8
velocette
Senior Member
 
Join Date: May 25, 2007
Location: South Florida
Posts: 823
300 grades of stainless (austenitic) steel are considered to be "faintly" magnetic, that is they will be attracted to a magnet very little. 400 grade stainless steel (Martensitic) is definitely magnetic and will be attracted by a magnet.
The difference is in the Nickel content in 300 grade versus little or none in 400 400 is also heat treatable which is why is used in firearms.
304 grade, the old reliable 18 & 8 (approximately 18% chromium & 8% Nickel, balance carbon steel.) with varying amounts of carbon mainly for post weld corrosion prevention.

Roger
__________________
Trigger control + Breath control + Sight alignment = Gun Control.
http://www.hrpclub.info/
NRA Smallbore Prone Master
velocette is offline  
Reply

Thread Tools

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT -5. The time now is 06:49 PM.


Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2014, vBulletin Solutions, Inc.
This site and contents, including all posts, Copyright © 1998-2013 S.W.A.T. Magazine
Copyright Complaints: Please direct DMCA Takedown Notices to the registered agent: thefiringline.com
Contact Us
Page generated in 0.07069 seconds with 7 queries