Old September 18, 2009, 11:16 AM   #1
Model-P
Senior Member
 
Join Date: February 24, 2009
Posts: 727
Purity of lead for cap-and-ball

I know that the ideal is 100% lead, but I usually add 2% tin for my 45 Colt cartridge loads. Would this also be O.K. for cap-and-ball round balls, or does 2% add a fair amount of hardness. I only add the tin to help with ease of moulding, and would rather not have to have another separate lead pot for my cap-and-ball lead. Thoughts?
Model-P is offline  
Old September 18, 2009, 03:03 PM   #2
Hawg
Senior Member
 
Join Date: September 8, 2007
Location: Mississippi
Posts: 16,177
It should be ok. I use lead that's 99.5% pure. As long as it isn't too hard to load it'll be fine.
Hawg is offline  
Old September 18, 2009, 03:16 PM   #3
sundance44s
Senior Member
 
Join Date: February 6, 2006
Location: Hernando , Ms.
Posts: 579
Your revolver loading levers will tell you when your lead is too hard .
Expecially the loading lever on the 1858 Remingtons ....the loading lever is held together by little pins ....they`ll snap like shear pins if the ball lead is too hard ........ask me how I know this ..
sundance44s is offline  
Old September 19, 2009, 07:41 PM   #4
Andy Griffith
Senior Member
 
Join Date: May 14, 2009
Location: Macon Co. NC
Posts: 591
If you load off the frame with one of the heavy-duty cylinder loaders, I don't think it matters so much.

If your only way to load is with the lever on the gun, you must keep it soft.
__________________
Barney Fife: "Nip it, nip it, nip it!"
Andy Griffith:"Oh now Barn'...."
Andy Griffith is offline  
Old September 19, 2009, 07:49 PM   #5
Model-P
Senior Member
 
Join Date: February 24, 2009
Posts: 727
Thankyou.
Does anyone know if 2% makes much difference?
Model-P is offline  
Old September 20, 2009, 01:24 AM   #6
Smokin_Gun
Senior Member
 
Join Date: December 4, 2005
Location: Mojave Desert, CA
Posts: 1,195
I never use anything but Soft Lead no additives ... but my thoughts from using only pure lead suggest to me tin is not needed.
The differance I would say is in loading the ball and cuttin' about a .0005" - .002" ring off the ball easily without hurtin' yer hand...
__________________
"I Smoke Black Powder" "Favor an 1858 Remington"
SGT. Smokin' Gun, Mosby's Rangers 43rd Virginia Cavalry C.S.A.
SASS# 19634, ...
Admin:http://blackpowdersmoke.com/oldcoots/index.php
Smokin_Gun is offline  
Old September 20, 2009, 08:11 PM   #7
robhof
Senior Member
 
Join Date: September 16, 2007
Posts: 712
robhof

2% tin shouldn't add too much hardness as long as they are air cooled and not quenched. Antimony and arsenic are the primary hardening additives to lead. Antimony is the desired additive in linotype. If you have to quench when you cast as I do, you can de-temper by placing the tempered slugs in a 350 to 375 degree oven for 30 min. and allow to cool to room temp in the oven. I use that process for all my b/p slugs, so I can cast a large amt. and drop in a 5 gal bucket of water and not worry about escaping hot slugs dropping onto insulation material. Ask me how I know- to borrow a phrase.
robhof is offline  
Old September 21, 2009, 12:31 AM   #8
Model-P
Senior Member
 
Join Date: February 24, 2009
Posts: 727
Thankyou. I guess I'll see if the loading lever complains too much about it. I don't quench, so that is good in this case.
Model-P is offline  
Old September 25, 2009, 11:08 PM   #9
sc928porsche
Senior Member
 
Join Date: May 29, 2008
Location: now living in alabama
Posts: 2,433
Hummmmmmmmmm....wheel weight works good for me.
__________________
No such thing as a stupid question. What is stupid is not asking it.
sc928porsche is offline  
Reply

Thread Tools Search this Thread
Search this Thread:

Advanced Search

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump


All times are GMT -5. The time now is 07:26 PM.


Powered by vBulletin® Version 3.8.7
Copyright ©2000 - 2024, vBulletin Solutions, Inc.
This site and contents, including all posts, Copyright © 1998-2021 S.W.A.T. Magazine
Copyright Complaints: Please direct DMCA Takedown Notices to the registered agent: thefiringline.com
Page generated in 0.04534 seconds with 8 queries