Refinishing S&W 39-2 NEED HELP!
I am going to refinish an old S&W 39-2 9mm and I need some suggestions on how to redo the frame. It is made of what looks like aluminum alloy. It looks like it has been carried in a leather hoster and the finish is gone off both sides if the frame. My question is can it be stripped down and repainted? If so what would be the best paint the use? Would DuraCoat work on Aluminum? Any help would be appreciated.
|
March 3, 2013, 10:31 AM | #2 |
Staff
Join Date: November 2, 1998
Location: Colorado
Posts: 21,840
|
You can't blue aluminum. Dipping aluminum parts will dissolve it in the bluing salts. Send it out to Cerrakote it instead. It's more durable that Duracote.
Trinidad College now does that. We've two instructors who went there to get certified as Cerrakote instructors. ETA: If I had to do it myself, I'd go Duracote.
__________________
Vigilantibus et non dormientibus jura subveniunt. Molon Labe! |
March 3, 2013, 10:42 AM | #3 |
Member
Join Date: February 24, 2008
Location: Alabama
Posts: 26
|
Im guessing that something like that would cost more then the gun is worth?! Really wanted to find something I could DIY.
|
March 3, 2013, 11:04 AM | #4 |
Senior Member
Join Date: January 15, 2013
Location: South Jersey
Posts: 1,416
|
Check out a local anodizer for the frame. There's lots of colors available if you want to get creative. But anything beyond DIY will probably wind up costing more that the gun is worth.
|
March 3, 2013, 12:11 PM | #5 |
Senior Member
Join Date: August 15, 2001
Posts: 129
|
If the frame is Aluminum, it was most likley originally Anodized, although the photo looks like it was painted with some type of enamal. I don't know about Cerrakote as I have no experience with it. I wouldn't waste my time with duracoat.
Yes, Aluminum can be refinished. We regularly refinish Aluminum parts with our TG-1 finish with no problems. However, it must be abrasive blasted as part of the refinish job to remove the old finish, scale, flaking finish, etc. Abrasive blasting Aluminum has to be done by somebody that has experience with it. If they use silica sand, it's very easy to ruin the part. (Frame, etc) Silica sand will "eat" Aluminum. Even freindly abrasives can damage it if it's shot at to high of a pressure or aimed at one spot for to long. The idea is to remove all paints and matte the surface, not cause scallops. It's a good idea to use some type of chemical Anodizing procedure on it before it's coated. We use Alodine. Depending on who you talk to, it's not quite as hard as "normal" Anodizing or it's harder. Keep yer powder dry, Mac. Tuff-Gun Finishes. The Name Says It All. Mac's Shootin' Irons http://www.shootiniron.com |
March 3, 2013, 12:21 PM | #6 |
Junior Member
Join Date: February 23, 2013
Posts: 3
|
Brownells
Contact Brownells. They have several different products for aluminum. None are as durable as Ceracote as mentioned earlier but more DIY friendly.
|
March 4, 2013, 04:59 PM | #7 |
Senior Member
Join Date: January 24, 2011
Location: Monroe,NC
Posts: 669
|
"Contact Brownells. They have several different products for aluminum. None are as durable as Ceracote as mentioned earlier but more DIY friendly"
Go to Brownells and get thier bake on finish in a spray can, spray it and bake it and your done. No need for a airbrush for one gun. Ceracote is not that hard if you have a airbrush.
__________________
The man that die's with the most stuff win's! |
March 5, 2013, 07:21 PM | #8 |
Senior Member
Join Date: March 1, 2000
Location: Boise, ID
Posts: 8,518
|
Brownell has a product called something like "Alumahyde", which is intended as a finish for aluminum.
I've use their spray 'n' bake teflon/moly finish, and works pretty well. |
March 5, 2013, 10:05 PM | #9 |
Member In Memoriam
Join Date: March 17, 1999
Posts: 24,383
|
I have used Alumahyde. Maybe there is a secret I don't know, but it seemed to be sort of a "cold blue" for aluminum alloy and was not at all durable, rubbing off easily. I suspect that like cold blue it might work to cover a scratch or ding, but not for anything like a large surface.
Jim |
|
|