October 2, 2012, 02:19 PM | #1 |
Senior Member
Join Date: June 16, 2011
Location: Ohio
Posts: 1,497
|
Gah! Why am I still leading?
Original load:
4.4 grains Bullseye 125gr MBC Roundnose OAL 1.13 Supposedly well within specs for both gun and bullet according to Alliant powder manual. But was getting a lot, and I mean a lot, of lead in the barrel. So badly that I had strips of it hanging from the rifling after 150 rounds. I dropped the powder load significantly and reduced OAL. Current load: 3.8 grains Bullseye 125gr MBC RN OAL 1.10 50 rounds and there is still some lead smearing on the lands. If nothing else, it's better than it was, but still not what I would consider acceptable. I did slug the barrel and got .355 on the button, give or take .0001 or so. A .356 bullet should be fine, shouldn't it?
__________________
"The best diplomat I know is a fully charged phaser bank" - Montgomery Scott |
October 2, 2012, 04:07 PM | #2 |
Senior Member
Join Date: May 26, 2008
Posts: 472
|
Put some bullets in a baggie, put in a half dozen drops of Alox, swish it around, dump them out on wax paper, let them dry over nite, your leading will be over---I take it this a 9mm???
I use 3.5 grs. of Bullseye pushing the 125 gr. MB--no leading in all three of my 9's. |
October 2, 2012, 04:24 PM | #3 |
Senior Member
Join Date: December 24, 2008
Location: Loveland, CO
Posts: 1,476
|
Your bullets are pretty hard. I would expect the faster loads to work better.
I would tend to use a slow powder, but that is just me. Did you clean out all of the copper in the barrel before you started shooting lead? That can cause leading. |
October 2, 2012, 07:54 PM | #4 |
Member in memoriam
Join Date: April 9, 2009
Location: Blue River Wisconsin, in
Posts: 3,144
|
I agree with jepp2, clean your barrel, scour that thing till it's mirror bright and operating room clean. Then go back to your 4.4 grains and I bet you will be fine.
__________________
Good intentions will always be pleaded for any assumption of power. The Constitution was made to guard the people against the dangers of good intentions. There are men in all ages who mean to govern will, but they mean to govern. They promise to be good masters, but they mean to be masters. --Daniel Webster-- |
October 2, 2012, 08:55 PM | #5 | |
Senior Member
Join Date: December 24, 2010
Location: Canada
Posts: 382
|
Quote:
What kind of gun is it? The lead I shoot through my CZs is .358" - a lot bigger than .356". Also keep in mind that commercial lead bullets often have a harder lube than desirable for handgun applications. The tumble lube suggestion by the other poster (floydster) might actually give you some improvement. Also where is the leading occurring in your barrel? More at the muzzle end or more toward the chamber? You shouldn't have to put up with leading at all when using lead bullets. I can literally shoot thousands through my barrel without cleaning it, and I still just use a patch when I want it to look extra pretty. |
|
October 2, 2012, 09:17 PM | #6 |
Junior member
Join Date: November 12, 2000
Location: Colorado Springs, Colorado
Posts: 9,494
|
Going to a .357 bullet would also help.
|
October 3, 2012, 03:05 AM | #7 |
Senior Member
Join Date: October 2, 2007
Posts: 641
|
sf, 10/3/12
When I started reloading I had problems with turning a rifled pistol barrel into a smoothbore within twenty rounds. And this was after I thought I'd done everything right. With the help of the gentlemen at www.castboolits.gunloads.com and here I figured out the problem. First make sure you are measuring your barrel slug with a micrometer and not a caliper. That small bit of inaccuracy in the caliper's measurement can make a big difference. Second, measure the bullet diameter before loading it (as you have done) and then pull the bullet after reloading it into a cartridge. Often there is enough swaging of the bullet when being pushed into the brass and then crimped that the bullet ends up undersized. My bullets would start out at 1-2 thousandths oversize before loading and end up 1 thousandth of an inch undersize after being pulled, which means I had lots of hot gas spraying past the undersized bullet and causing leading. The primary problem with leading is usually bullet fit/size. Other factors like lube type, lube groove type (ie, tumble lube vs. conventional grooves), bullet speed and hardness are usually addressed once bullet-barrel fit is optimal. To overcome my bullet swaging problem I just ordered an Accurate Mold Company mold (both .45 and 9mm and 44 special) at two thousandths over barrel diameter and they drop into my brass without sizing (usually at requested size to one-half a thousandths oversize) and leave no leading whatsoever in the barrel. So for my 9mm I use bullets at .357-.358, .45 at .453 and 44 special at .432-423". Good luck and check out the castboolits.gunloads.com site- it's a great site for reloaders. best wishes- oldandslow |
October 3, 2012, 12:09 PM | #8 | ||||
Senior Member
Join Date: June 16, 2011
Location: Ohio
Posts: 1,497
|
Quote:
Quote:
Quote:
Quote:
Any thoughts on where to find .357 9mm bullets? Just use .357s or what?
__________________
"The best diplomat I know is a fully charged phaser bank" - Montgomery Scott |
||||
October 3, 2012, 01:12 PM | #9 |
Member in memoriam
Join Date: April 9, 2009
Location: Blue River Wisconsin, in
Posts: 3,144
|
Maybe time for KG12 or Tubbs Final Finish. You should not be leading at all or very little.
__________________
Good intentions will always be pleaded for any assumption of power. The Constitution was made to guard the people against the dangers of good intentions. There are men in all ages who mean to govern will, but they mean to govern. They promise to be good masters, but they mean to be masters. --Daniel Webster-- |
October 3, 2012, 03:38 PM | #10 | |
Senior Member
Join Date: December 24, 2010
Location: Canada
Posts: 382
|
Quote:
|
|
October 3, 2012, 04:02 PM | #11 | |
Senior Member
Join Date: June 16, 2011
Location: Ohio
Posts: 1,497
|
Best I can tell, it slugged right at .355
Will try Alox if I can find any. Quote:
Any chance it could be the alloy/makeup of the bullets themselves?
__________________
"The best diplomat I know is a fully charged phaser bank" - Montgomery Scott |
|
October 3, 2012, 04:31 PM | #12 |
Senior Member
Join Date: May 12, 2011
Location: New Mexico
Posts: 1,315
|
I think the only way to get leading at those levels is with unlubed bullets. Can you see lube in the groove? I shoot lead pre-lubed with the blue lube. Leading is never a problem. You must be frustrated as h--- after cleaning that thoroughly, just to get leaded again.
|
October 3, 2012, 04:42 PM | #13 |
Senior Member
Join Date: December 24, 2010
Location: Canada
Posts: 382
|
Stressfire, perhaps it's only the 92fs European (Italian) made guns that have such huge bores because they are notorious for having this issue - like 358" which is a heck of a lot bigger than .355". I don't know anyone up here with the US made version because frankly they're not much in demand.
But that makes your leading problem even more mysterious.... Edit: But now other questions now come to mind... like how are you loading these? Are you using crimp or Lee FCD? Have you pulled a bullet and measured it along its base to where it fits into the case? Last edited by Gerry; October 3, 2012 at 04:59 PM. |
October 3, 2012, 05:30 PM | #14 |
Senior Member
Join Date: October 24, 2008
Location: GATOR COUNTRY HA HA HA!
Posts: 721
|
I've shot the MB 125 Smallball in 3 of my 9's without leading at all. That's with Unique ; )
Y/D
__________________
There's a GATOR in the bushes & She's Callin my name >Molly Hatchett< |
October 3, 2012, 05:38 PM | #15 |
Senior Member
Join Date: August 25, 2008
Location: In the valley above the plain
Posts: 13,424
|
Try a slower burn rate powder. (AA#2, Unique, 231, etc.)
__________________
Don't even try it. It's even worse than the internet would lead you to believe. |
October 3, 2012, 06:16 PM | #16 |
Senior Member
Join Date: December 26, 2004
Location: Louisville KY
Posts: 13,806
|
Are they keyholing?
Definitely go .357 though, if not .358. |
October 3, 2012, 06:53 PM | #17 | |||
Senior Member
Join Date: June 16, 2011
Location: Ohio
Posts: 1,497
|
Quote:
Quote:
Quote:
__________________
"The best diplomat I know is a fully charged phaser bank" - Montgomery Scott |
|||
October 3, 2012, 08:00 PM | #18 | ||
Member in memoriam
Join Date: April 9, 2009
Location: Blue River Wisconsin, in
Posts: 3,144
|
Quote:
Quote:
http://www.kgcoatings.com/cleaning/k...-bore-cleaner/ Tubbs Final Finish is a bore cleaning and polishing kit. Makes a smooth barrel making it hard for lead to grab hold and cling to it. I'm betting looking through it with a naked eye and a light it looks pretty good but a borescope would show you some imperfections you can't see any other way. http://www.davidtubb.com/final-finish-tms
__________________
Good intentions will always be pleaded for any assumption of power. The Constitution was made to guard the people against the dangers of good intentions. There are men in all ages who mean to govern will, but they mean to govern. They promise to be good masters, but they mean to be masters. --Daniel Webster-- |
||
October 3, 2012, 08:22 PM | #19 |
Senior Member
Join Date: October 24, 2008
Location: GATOR COUNTRY HA HA HA!
Posts: 721
|
"[FrankenMauser Try a slower burn rate powder. (AA#2, Unique, 231, etc.)]"
That would be a good start, As peak preasure would be as the boolits Is alredy started down barrle more IMO ; ) Y/D
__________________
There's a GATOR in the bushes & She's Callin my name >Molly Hatchett< |
October 3, 2012, 11:49 PM | #20 | |
Senior Member
Join Date: August 25, 2008
Location: In the valley above the plain
Posts: 13,424
|
Quote:
__________________
Don't even try it. It's even worse than the internet would lead you to believe. |
|
October 4, 2012, 08:11 AM | #21 |
Senior Member
Join Date: June 16, 2011
Location: Ohio
Posts: 1,497
|
Did not get a chance to check or do anything last night...darn women and their needs for "us time"
Anyways, will hopefully get to check everything out tonight - should the bullet be getting swaged down during seating, what is done to correct that? Just back off the crimp a bit?
__________________
"The best diplomat I know is a fully charged phaser bank" - Montgomery Scott |
October 4, 2012, 02:20 PM | #22 |
Senior Member
Join Date: August 25, 2008
Location: In the valley above the plain
Posts: 13,424
|
The bullets shouldn't be getting drawn down or shaved during seating.
Make sure you're expanding the cases far enough, and try crimping in a separate step.
__________________
Don't even try it. It's even worse than the internet would lead you to believe. |
October 4, 2012, 02:34 PM | #23 | |
Senior Member
Join Date: July 28, 2007
Location: Ohio
Posts: 11,756
|
Quote:
AA#2 is a scorching fast powder, like Titegroup.
__________________
Attention Brass rats and other reloaders: I really need .327 Federal Magnum brass, no lot size too small. Tell me what caliber you need and I'll see what I have to swap. PM me and we'll discuss. |
|
October 4, 2012, 05:56 PM | #24 |
Member
Join Date: August 1, 2012
Location: Florida
Posts: 98
|
I have great luck with tightgroup in everything ive tried it in.
|
October 6, 2012, 08:31 AM | #25 |
Senior Member
Join Date: May 26, 2008
Posts: 472
|
For me Titegroup and cast bullets do not mix--powder is too hot.
Smokeyloads |
|
|