Although I've not tried it, I'd tend to think it might crack from the neck being squeezed down to another diameter. Maybe it would be OK for your application due to the fact that you are only going from 30 to 7 mm. That nickel has to go someplace when it is formed down though. Maybe you would have problems if it were a more drastic reduction in caliber.
Anybody else try this?
|