Federal brass is [notoriously] soft and will begin to flow at levels that other brass would withstand [more] easily.
It's still "good" and you can reuse it, ...but at lower levels. Eventual primer pocket looseness will tell you when to discard. (And do not oversize. Just enough that cases will chamber reliably, no more)
|